Influence of CO2 Laser Irradiation and CPPACP Paste Application on Demineralized Enamel Microhardness
Abstract
Introduction: It has been suggested that the application of casein phosphopeptide-amorphous calcium phosphate paste (CPP-ACP) and CO2 laser irradiation on enamel could increase the resistance of enamel to caries and acid attacks. The aim of the current study was to compare the influence of CPP-ACP paste application and irradiation of CO2 laser on microhardness of demineralized enamel. Methods: Thirty sound maxillary extracted premolars were selected. The crowns were cut at the cervical line and were split into facial and palatal halves. Specimens were mounted in selfcure acrylic blocks in such way that the enamel surface was exposed to 4×4 mm. After a pH cycling of the specimens, they were randomly divided into 4 groups (n=15), as follows: CG: Control group, LAS: CO2 laser, CP: CPP-ACP and LASCP: laser combined CPP-ACP treatment. The Vickers microhardness of the specimens was measured (500 g load, 5 seconds, 3 points). Data were analyzed using one-way ANOVA and post hoc Tukey tests (α =0.05). Results: The lowest mean Vickers microhardness value was observed in CG group (192.57±50.87 kg/mm2 ) and the highest in LASCP group (361.86±22.22 kg/mm2 ). There were significant differences between groups (P<0.001). The pairwise compariso...Continue Reading
References
Acquired acid resistance of enamel and dentin by CO2 laser irradiation with sodium fluoride solution
Thermal and chemical modification of dentin by 9-11-microm CO2 laser pulses of 5-100-micros duration
Microhardness and SEM after CO(2) laser irradiation or fluoride treatment in human and bovine enamel
Citations
Related Concepts
Related Feeds
Birth Defects
Birth defects encompass structural and functional alterations that occur during embryonic or fetal development and are present since birth. The cause may be genetic, environmental or unknown and can result in physical and/or mental impairment. Here is the latest research on birth defects.