Microstructure and selected mechanical properties of aged Ti-15Zr-based alloys for biomedical applications

Materials Science & Engineering. C, Materials for Biological Applications
Diego R N CorreaCarlos R Grandini

Abstract

In this study, Ti-15Zr-xMo (5, 10, 15, and 20 wt%) alloys were submitted to solution and aging treatments and their effects evaluated in terms of phase composition and selected mechanical properties (Vickers microhardness and Young's modulus) for use as biomedical implants. The solution treatment was performed at 1123 K for 2 h, while aging treatments were carried out at 698 K for 4, 8, and 12 h, followed by water quenching. Phase composition and microstructure were dependent of the heat treatments, with Ti-15Zr-5Mo (α + β type) and Ti-15Zr-10Mo (metastable β type) alloys exhibiting intense α phase precipitation. The α-phase precipitates were related to α″ → α and β → α phase decompositions. The Ti-15Zr-10Mo alloy exhibited an intermediary isothermal ω-phase precipitation after aging for 4 h. Vickers microhardness and Young's modulus values changed gradually with the amount of α phase. Aged Ti-15Zr-15Mo and Ti-15Zr-20Mo alloys presented better combinations of hardness and Young's modulus than CP-Ti and Ti-64 ELI for biomedical applications.

Citations


❮ Previous
Next ❯

Related Concepts

Related Feeds

Birth Defects

Birth defects encompass structural and functional alterations that occur during embryonic or fetal development and are present since birth. The cause may be genetic, environmental or unknown and can result in physical and/or mental impairment. Here is the latest research on birth defects.